Study on Effect of Welding Parameters on Weld Bead Geometry of AC TIG Welding in Aluminium

Authors

  • Niramay Ghosh Mechanical Engineering Department, Asansol Engineering College, Asansol, India
  • Santanu Das Department of Mechanical Engineering, Kalyani Govt. Engineering College, Kalyani, India

Keywords:

Aluminium, TIG Welding, Visual Bead Inspection, Penetration, Bead Width, Bending Test, Micro Hardness Test

Abstract

Aluminium and aluminium alloys have large uses in different industries due to its higher strength to weight ratio. Due to controllable heat input and filler consumption Tungsten Inert Gas Welding (TIG) is widely used in aluminium welding. In this work, bead geometry of Al 6060 alloy have been studied in different AC TIG welding parameters, like welding current, welding speed etc. Butt joint was performed. From the observation, it is found out that at a current 177, 190 and 200 A with a welding speed of 110, 130 and 150 mm/min respectively, good depth of penetration can be achieved, and hence, this condition can be used for joining aluminium alloy satisfactorily.

Metrics

PDF views
31
Jan 2020Jul 2020Jan 2021Jul 2021Jan 2022Jul 2022Jan 2023Jul 2023Jan 2024Jul 2024Jan 2025Jul 2025Jan 202610
|

Downloads

Published

01-09-2019

How to Cite

Ghosh , N., & Das, S. (2019). Study on Effect of Welding Parameters on Weld Bead Geometry of AC TIG Welding in Aluminium. Manufacturing Technology Today, 18(9), 30–38. Retrieved from https://mtt.cmti.res.in/index.php/journal/article/view/176

Issue

Vol. 18 No. 9 (2019): September 2019

Section

Articles

License

All the articles published in Manufacturing Technology Today (MTT) Journal are held by the Publisher. Central Manufacturing Technology Institute (CMTI) as a publisher requires its authors to transfer the copyright prior to publication. This will permit CMTI to reproduce, publish, distribute, and archive the article in print and electronic form and also to defend against any improper use of the article.